K11 polymer modified cement waterproof waterproof material / water-based waterproof coating

K11 Polymer Modified Cement Waterproof Slurry Overview:This product is a kind of high-performance waterproof material, which is made of cement and fine aggregate as main raw materials, high-quality polymer and a variety of additives as modified materials. This product not only has excellent waterproof performance,

Featured Products

K11 Polymer Modified Cement Waterproof Slurry

K11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof Coating 

Overview:

This product is a kind of high-performance waterproof material, which is made of cement and fine aggregate as main raw materials, high-quality polymer and a variety of additives as modified materials. This product not only has excellent waterproof performance, it also contains some active compounds in the material. This active compound can penetrate into the interior of the substrate, and produce micro expansion crystals in the gap cracks inside the substrate, so as to improve the self compactness of the substrate and seal the water penetration, as to eliminate the leakage problem.

 

Features:

1. Good adhesion performance.

2. Convenient in construction, can be carried out the construction under the wet (no open water) foundation, and shorter construction period.

3. Corrosion resistance, high temperature resistance, low temperature resistance and aging resistance.

4. No deterioration, anti-seismic crack, non-toxic, harmless, tasteless, no pollution to the environment.

5. If the structure is not damaged or by human being, it can have the same self-life as the building.

6. Decorative layer (such as paint, ceramic tile, etc.) can be applied directly on the waterproof layer.

 

Scope of Application:

1. Indoor and outdoor cement concrete structure, wall brick, light brick wall structure.

2. Food-graded pool, swimming pool, fish pool, sewage treatment pool.

3. Reservoir dam, tunnel, bridge, ice store, bathroom, sink, canal, floor heating waterproof, moisture-proof, seepage proof.

4. Wall, floor, building foundation, exterior wall, basement, toilet and balcony.

5. The binder of polyphenylene board has impermeability and can also be used as interface treatment agent.

 

Performance Index:

Executive standard: JC/T2090-2011

Serial number

Items

Technical Indicators

Type I

-

1

Drying time a / h

Dry time ≤

4

Dry time ≤

8

2

Impermeability pressure MPa ≥

0.5

0.6

3

Impervious to water, 0.3MPa, 30min

-

impermeable

4

Flexibility

Transverse deformation capacity / mm ≥

02.0

-

Bending

-

No crack

5

Bond strength / MPa

No treatment ≥

0.7

Wet base layer ≥

0.7

Alkali treatment ≥

0.7

Immersion treatment ≥

0.7

6

Compressive strength / MPa ≥

12.0

-

7

Flexural strength / MPa ≥

1.0

-

 

Key Points Of Construction:

1. The base surface must be flat, firm, clean, free of water and leakage; the defects such as unevenness and cracks must be filled and leveled, and water of the leakage area must be stopped; the internal and external corners should be made into arc angles.

 

2. Wet the treated base surface with water (no water is required), and measure it accurately according to the mixing ratio required by the factory. When mixing, mix the liquid material (or water) with a mixer, slowly add the powder and keep mixing, until the powder fully stir and disperse with no powder kind and no precipitation. The prepared mixture material should be used up within 1 hour.

 

3. Finish layer by layer according to the selected construction method, and the interval time between each layer shall be subject to the previous layer being dry and not adhering. Generally, it takes more than 4 hours for the unmanned construction, and more than 8 hours for the manned construction (the temperature is 20°C). If the temperature is low, the humidity and the ventilation is bad, then it would take longer time to dry).

 

4. Material: About 2.5kg per square meter (1.5mm thick).

 

5. Please do not work when the environmental temperature under 5°C or in rain, and do not work in humid air circulation environment.

 

Model:

K11 Polymer Modified Cement Waterproof Slurry (18KG Barrel Pack)

TH-FT-K11(JJ)18K

18Kg/Barrel

K11 Polymer Modified Cement Waterproof Slurry (20KG Barrel Pack)

TH-FT-K11(JJ)20K

20Kg/Barrel

 
K11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof CoatingK11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof CoatingK11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof Coating

K11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof CoatingK11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof CoatingK11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof Coating 
K11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof CoatingK11 Polymer Modified Cement Waterproof Waterproofing Material/Water Based Waterproof Coating